IS 320 HT1 or HT2 High Tensil Leaded Brass

Product Description

IS 320 HT1 or HT2 High Tensil Leaded Brass

 

We are one of the leading manufacturers, exporters and suppliers of a premium quality assortment of High Tensile Brass Rods, Brass Extrusion Rods. Offered in different sizes, thicknesses and grades, these are valued for their excellent performance, high conductivity, durability, reliable operation and corrosion resistance. At par with the prerequisite industry standards, our High Tensile Brass Rods can be purchased by clients in standard & customized specifications and at cost effective rates.

Specification :
High Tensile Brass	IS 320 HT1 or HT2 BS 2874 CZ114 or CZ115 JIS 3250H C6782 or C6783

Specifics :

• BS:1001

• HT12472

• IS:320 l & ll

Chemical Requirements		HT1		HT2
Copper		56.0 - 60.0%		56.0 - 61.0%
Lead		0.20 to 1.50%		0.50 to 1.50%
Iron		0.20 to 1.25%		0.20 to 1.50%
Tin		0.20 to 1.0%		1.0% max
Aluminum		0.2% max		0.30 to 2%
Manganese		0.25 - 2.0%		0.50-2.0%
Total Imp.		0.50% max		0.50% max
Zinc		Remainder		Remainder
Physical Properties
Condition	Size	T.S. MPa	EL% Min	T.S. MPa	EL% Min
As manufactured	All Size	430 min	20%	460 min	20%
Cold-worked & Stress	10-40	480 min	12%	520 min	12%
Relieved	40 above			500 min	15%
Fabrication Properties
Capacity for being
Cold formed		Poor		Fair
Hot worked		Good		Good
Machinability Rating		30%		30%
Resistance to Corrosion		Excellent		Excellent
Suitability for soldering		Excellent		Fair
Uses
HT1 is suitable for Soldering
Ht2 is suitable for Machining

 

Versatile Performance and Reliability

These high tensile leaded brass rods deliver dependable mechanical strength and durability, making them ideal for various sectors, including automotive, electrical, and engineering. Their blend of excellent corrosion resistance and good conductivity supports both structural and conductive applications, while their machinability facilitates efficient fabrication.


Precision Manufacturing and Quality Assurance

Manufactured under strict IS 320 standards, these rods undergo rigorous quality controls to ensure consistent properties such as weight, tolerance, and shape. Their half-hard temper optimizes them for a balanced combination of strength and flexibility, while dimensional tolerances of +/- 0.1mm support exacting requirements in advanced industries.